Virgin Plastics Polypropylene PP Manufacturer Granules Raw Material PP with Best Price

Product Description

JINGBO Brand INJECTION POLYPROPYLENE HOMOPOLYMER (HP500N/HP500P)
Product Description:
Medium melt index homopolymer polypropylene resin has the advantages og high rigidity and good heat resistance deformation temperature. It's widly used in small household appliances such as electric kettles, rice cookers,hair dryers, and injection molding of household and toy priducts.

		Unit	HP500N	HP500P
Melt mass-flow rate(MFR)		g/10min	11.6	18.2
Isotactic Index		%	98.0	97.0
Ash content(mass fraction )		%	0.011	0.015
Yellow index		/	-2.4	-2.8
	Tensile yield stress	MPa	34.0	34.5
Flexural modulus		MPa	1561	1723
Charpy notched impact(23ºC)		kJ/m2	2.6	2.4
Load deformation temperature		ºC	95	97
Molding shrinkage(SMp)		%	1.2	1.2
Molding shrinkage(SMn)		%	1.2	1.2

 

      Polypropylene, referred to as PP, is a polymer made of propylene by addition polymerization. White waxy material, transparent and light in appearance. The chemical formula is (C3H6)n, the density is 0.89 ~ 0.91g/cm3, flammable, the melting point is 164~170 ° C, the softening is about 155 ° C, and the temperature range is -30 ~ 140 ° C. It can resist the corrosion of acid, alkali, salt solution and a variety of organic solvents below 80ºC, and can decompose under high temperature and oxidation.
     Polypropylene is a thermoplastic synthetic resin with excellent performance. It is a colorless semi-transparent thermoplastic lightweight general plastic with chemical resistance, heat resistance, electrical insulation, high strength mechanical properties and good high wear resistance. It is widely used in the production of clothing, blankets and other fiber products, medical equipment, automobiles, bicycles, spare parts, transportation pipes, chemical containers and so on. It is also used for food and medicine packaging.

 

Film Grade
Item	Test condition	Test Method	Value	Unit
Density		ISO 1183	0.944-0.955	g/cm3
MFR	190°C/2.16kg	ISO 1133	0.03-0.07	g/10min
Tensile strength at yield		ISO 527-2	22	MPa
Elongation at break		ISO 527-2	>350	%
ESCR	F50,50°C,100%	ASTM D-1693A	1000	h
VICAT		ASTM D-1525	126	°C
Blown Grade
Item	Test Condition	Test Method	Value	Unit
Density		ISO 1183	0.950~0.955	g/cm
MFR	190°C/2.16kg	ISO 1133	1.7~2.5	g/10min
Tensile strength at yield		ISO 527-2	24	MPa
Elongation at break		ISO 527-2	>600	%
Injection grade
Item	Test Condition	Test Method	Value	Unit
MFR	190°C/2.16kg	ASTM D-1238	20	g/10min
Density	---	ASTM D-792	0.954	g/cm3
Tensile strength at yiled	---	ASTM D-638	28	MPa
Elongation at break	---	ASTM D-638	250	%
Impact tensile strength	---	ASTM D-1822	42	kJ/m2
ESCR		ASTM D-1693	3	---
VACIT	---	ASTM D-1525	127	°C

 

FAQ

 

1. About Quality
All the products must be tested strictly according to the testing procedure before shipment.

2. About Delivery Period
Normally delivered in 7 working days after the confirmation of order& payment.   And it varies according to the material and quantity.

3. About Payment Term
It's flexible, T/T, L/C at sight.

4. About the mode of transportation
(1) by sea
(2) by train

5. If I order in large quantities, can the price be lower?
A: Yes, we can offer a discount for large orders.