China Brand Raffia Grade Raw Material Polypropylene Resin Hengli PP Yarn L5e89 Mfr3 100% Virgin Granules

• Feature: Biodegradable
• Material: Polypropylene/PP
• Usage: Plastic Products
• Model NO.: PP L5E89
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection Grade. Extrusion Grade, Injection
• Color: White
• Other Name: Polypropylene Particle PP
• ODM/OEM: Accepted
• Keyword: Polypropylene Resin Virgin PP
• Delivery Time: 5-7 Working Days
• Appearance: Transparent Granule
• Transport Package: 25kg/Bag
• Specification: 100% Virgin PP
• Origin: China
• HS Code: 3902100090
• Production Capacity: 8000tons/Months

Product Description

      Polypropylene, referred to as PP, is a polymer made of propylene by addition polymerization. White waxy material, transparent and light in appearance. The chemical formula is (C3H6)n, the density is 0.89 ~ 0.91g/cm3, flammable, the melting point is 164~170 ° C, the softening is about 155 ° C, and the temperature range is -30 ~ 140 ° C. It can resist the corrosion of acid, alkali, salt solution and a variety of organic solvents below 80ºC, and can decompose under high temperature and oxidation.

      Homo Polymer, Raffia Grade PP L5E89 is a natural colored granule with very good processability and low water carry-over. It adopts the advanced Unipol process of Grace Company of the United States. It is widely used to produce woven bags, applicable for textile, jumbo bags, carpet backing. It also can be used in food package, manufacturer have FDA certificate.

No.	Properties	Units	Typical Values	Test Methods
01	Melt Flow Rate(230ºC/2.16kg)	g/10min	3.21	GB/T 3682.1-2018
02	Isotactic Index	%	97.3	GB/T 2412-2008
03	Ash	% w/w	0.0211	GB/T 9345.1-2008
04	Yellowness Index	%	≤ 4	HG/T 3862-2006
05	Color Granule	pcs/kg	0	SH/T 1541.1-2019
06	Black Granule	pcs/kg	0	SH/T 1541.1-2019
07	Tensile Strength at Yield (50mm/min)	Mpa	32.4	GB/T 1040.2-2006
08	Tensile Strength at Break(50mm/min)	Mpa	23.4	GB/T 1040.2-2006
09	Nominal Tensile Strain at Break(50mm/min)	%	618	GB/T 1040.2-2006

Film Grade
Item	Test condition	Test Method	Value	Unit
Density		ISO 1183	0.944-0.955	g/cm3
MFR	190°C/2.16kg	ISO 1133	0.03-0.07	g/10min
Tensile strength at yield		ISO 527-2	22	MPa
Elongation at break		ISO 527-2	>350	%
ESCR	F50,50°C,100%	ASTM D-1693A	1000	h
VICAT		ASTM D-1525	126	°C
Blown Grade
Item	Test Condition	Test Method	Value	Unit
Density		ISO 1183	0.950~0.955	g/cm
MFR	190°C/2.16kg	ISO 1133	1.7~2.5	g/10min
Tensile strength at yield		ISO 527-2	24	MPa
Elongation at break		ISO 527-2	>600	%
Injection grade
Item	Test Condition	Test Method	Value	Unit
MFR	190°C/2.16kg	ASTM D-1238	20	g/10min
Density	---	ASTM D-792	0.954	g/cm3
Tensile strength at yiled	---	ASTM D-638	28	MPa
Elongation at break	---	ASTM D-638	250	%
Impact tensile strength	---	ASTM D-1822	42	kJ/m2
ESCR		ASTM D-1693	3	---
VACIT	---	ASTM D-1525	127	°C

 

FAQ

 

1. About Quality
All the products must be tested strictly according to the testing procedure before shipment.

2. About Delivery Period
Normally delivered in 7 working days after the confirmation of order& payment.   And it varies according to the material and quantity.

3. About Payment Term
It's flexible, T/T, L/C at sight.

4. About the mode of transportation
(1) by sea
(2) by train

5. If I order in large quantities, can the price be lower?
A: Yes, we can offer a discount for large orders.