Plastic Homopolymer Injection Molding Parts Zpc PP V30g Cheap Price Polypropylene Granules

• Feature: Biodegradable
• Material: Polypropylene/PP
• Usage: Plastic Products
• Model NO.: PP V30G
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection Grade. Extrusion Grade, Injection
• Color: White
• Other Name: Polypropylene Particle PP
• ODM/OEM: Accepted
• Keyword: Polypropylene Resin Virgin PP
• Delivery Time: 5-7 Working Days
• Appearance: Transparent Granule
• Transport Package: 25kg/Bag
• Specification: 100% Virgin PP
• Origin: China
• HS Code: 3902100090
• Production Capacity: 8000tons/Months

Product Description

      Polypropylene, referred to as PP, is a polymer made of propylene by addition polymerization. White waxy material, transparent and light in appearance. The chemical formula is (C3H6)n, the density is 0.89 ~ 0.91g/cm3, flammable, the melting point is 164~170 ° C, the softening is about 155 ° C, and the temperature range is -30 ~ 140 ° C. It can resist the corrosion of acid, alkali, salt solution and a variety of organic solvents below 80ºC, and can decompose under high temperature and oxidation.

 

       PP - V30G based on The the UnipolTM gas phase process technology of grace company to produce homopolymer polypropylene resin. The main raw material of the product is polymerization grade propylene, which is produced by polymerization, degassing, granulation, packaging and other processes with efficient catalyst. It is widely used to Lids and covers for thin-walled products,Various container,Toys.

No.	Property		Units	PP-H.Y.140-02-150 V30G
				Premium	First	Qualified
1	Appearance	Coloring	pcs/kg	≤5	≤10	≤20
		Black Pellets	pcs/kg	0
		Over or Undesized Pellets	g/kg	report
		Snakeskin granule and tailing granule	pcs/kg	report
2	Melt Flow Rate	Standard Value	g/10min	14.5
		Deviation		±2.5	±3	±3.5
3	Isotactic Index		%	95±1.5
4	Ash,(mass)		mg/kg	≤300
5	Tensile Property	Tensile Stress at Yield	MPa	≥31.0	≥30.0	≥29.0
		Tensile Stress at Break	MPa	≥8.00
6	Flexural modulus,(Ef)		MPa	report

Film Grade
Item	Test condition	Test Method	Value	Unit
Density		ISO 1183	0.944-0.955	g/cm3
MFR	190°C/2.16kg	ISO 1133	0.03-0.07	g/10min
Tensile strength at yield		ISO 527-2	22	MPa
Elongation at break		ISO 527-2	>350	%
ESCR	F50,50°C,100%	ASTM D-1693A	1000	h
VICAT		ASTM D-1525	126	°C
Blown Grade
Item	Test Condition	Test Method	Value	Unit
Density		ISO 1183	0.950~0.955	g/cm
MFR	190°C/2.16kg	ISO 1133	1.7~2.5	g/10min
Tensile strength at yield		ISO 527-2	24	MPa
Elongation at break		ISO 527-2	>600	%
Injection grade
Item	Test Condition	Test Method	Value	Unit
MFR	190°C/2.16kg	ASTM D-1238	20	g/10min
Density	---	ASTM D-792	0.954	g/cm3
Tensile strength at yiled	---	ASTM D-638	28	MPa
Elongation at break	---	ASTM D-638	250	%
Impact tensile strength	---	ASTM D-1822	42	kJ/m2
ESCR		ASTM D-1693	3	---
VACIT	---	ASTM D-1525	127	°C

 

FAQ

 

1. About Quality
All the products must be tested strictly according to the testing procedure before shipment.

2. About Delivery Period
Normally delivered in 7 working days after the confirmation of order& payment.   And it varies according to the material and quantity.

3. About Payment Term
It's flexible, T/T, L/C at sight.

4. About the mode of transportation
(1) by sea
(2) by train

5. If I order in large quantities, can the price be lower?
A: Yes, we can offer a discount for large orders.