Polypropylene PP-PA14D Copolymer Pipe Grade Plastic Raw Material PP Granules

• Feature: Biodegradable
• Material: Polypropylene/PP
• Usage: Plastic Products
• Model NO.: PP-PA14D
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection Grade. Extrusion Grade, Injection
• Color: White
• Other Name: Polypropylene Particle PP
• ODM/OEM: Accepted
• Keyword: Polypropylene Resin Virgin PP
• Delivery Time: 5-7 Working Days
• Appearance: Transparent Granule
• Transport Package: 25kg/Bag
• Specification: 100% Virgin PP
• Origin: China
• HS Code: 3902100090
• Production Capacity: 8000tons/Months

Product Description

      Polypropylene, referred to as PP, is a polymer made of propylene by addition polymerization. White waxy material, transparent and light in appearance. The chemical formula is (C3H6)n, the density is 0.89 ~ 0.91g/cm3, flammable, the melting point is 164~170 ° C, the softening is about 155 ° C, and the temperature range is -30 ~ 140 ° C. It can resist the corrosion of acid, alkali, salt solution and a variety of organic solvents below 80ºC, and can decompose under high temperature and oxidation.
     PP-PA14D is suitable for the production of hot and cold water pipes and direct drinking water pipes to 
ensure the water quality is free from secondary pollution.And can be used to transport edible liquids in beverage factories and chemical liquids in chemical plants. It also can be used in the fields of heating on the wall, snow melting devicefor norther buildings,used be in tubes for solar heating and cooling devices.All kinds of external air conditioner pipes, agricultural sprinkler irrigation pipes, also very suitable for using this materials.

No.	ITEM	UNIT	INDEX	RESULTS	TEST METHOD
01	Coloring	g/kg	≤ 10	0	SH/T 1541. 1
02	Big/small pellet	g/kg	≤ 100	21.1	SH/T 1541. 1
03	Yellow color Index	g/kg	≤ 10	0	SH/T 1541. 1
04	Melt mass flow rate(MFR)	g/10min	0.22-0.30	0.26	GB/T 3682. 1
05	Tensile yield stress	Mpa	>21.0	24.0	GB/T 1040.2
06	Flexural modulus(Ef)	Mpa	>600	669	GB/T 9341
07	Charpy notched impact strenth (-20ºC)	KJ/m2	≥ 1.8	2.2	GB/T 1043. 1
08	Charpy notched impact strenth (23ºC)	---	≤ 2.0	1.4	HG/T 3862

Film Grade
Item	Test condition	Test Method	Value	Unit
Density		ISO 1183	0.944-0.955	g/cm3
MFR	190°C/2.16kg	ISO 1133	0.03-0.07	g/10min
Tensile strength at yield		ISO 527-2	22	MPa
Elongation at break		ISO 527-2	>350	%
ESCR	F50,50°C,100%	ASTM D-1693A	1000	h
VICAT		ASTM D-1525	126	°C
Blown Grade
Item	Test Condition	Test Method	Value	Unit
Density		ISO 1183	0.950~0.955	g/cm
MFR	190°C/2.16kg	ISO 1133	1.7~2.5	g/10min
Tensile strength at yield		ISO 527-2	24	MPa
Elongation at break		ISO 527-2	>600	%
Injection grade
Item	Test Condition	Test Method	Value	Unit
MFR	190°C/2.16kg	ASTM D-1238	20	g/10min
Density	---	ASTM D-792	0.954	g/cm3
Tensile strength at yiled	---	ASTM D-638	28	MPa
Elongation at break	---	ASTM D-638	250	%
Impact tensile strength	---	ASTM D-1822	42	kJ/m2
ESCR		ASTM D-1693	3	---
VACIT	---	ASTM D-1525	127	°C

 

FAQ

 

1. About Quality
All the products must be tested strictly according to the testing procedure before shipment.

2. About Delivery Period
Normally delivered in 7 working days after the confirmation of order& payment.   And it varies according to the material and quantity.

3. About Payment Term
It's flexible, T/T, L/C at sight.

4. About the mode of transportation
(1) by sea
(2) by train

5. If I order in large quantities, can the price be lower?
A: Yes, we can offer a discount for large orders.