Hengli Ppb M09 Polypropylene Granules Plastics Material PP for Injection Molding Grade

• Feature: Biodegradable
• Material: Polypropylene/PP
• Usage: Plastic Products
• Model NO.: Hengli PPB M09
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection Grade. Extrusion Grade, Injection
• Color: White
• Other Name: Polypropylene Particle PP
• ODM/OEM: Accepted
• Keyword: Polypropylene Resin Virgin PP
• Delivery Time: 5-7 Working Days
• Appearance: Transparent Granule
• Transport Package: 25kg/Bag
• Specification: 100% Virgin PP
• Origin: China
• HS Code: 3902100090
• Production Capacity: 8000tons/Months

Product Description

      Polypropylene, referred to as PP, is a polymer made of propylene by addition polymerization. White waxy material, transparent and light in appearance. The chemical formula is (C3H6)n, the density is 0.89 ~ 0.91g/cm3, flammable, the melting point is 164~170 ° C, the softening is about 155 ° C, and the temperature range is -30 ~ 140 ° C. It can resist the corrosion of acid, alkali, salt solution and a variety of organic solvents below 80ºC, and can decompose under high temperature and oxidation.
      It is mainly used in thin-wall injection molding processing, and can be processedinto products, such as fast food boxes, packaging boxes, finishing boxes, cups, food containers and modified material of automobile.

No.	ITEM	UNIT	INDEX	TEST METHOD
01	Melt  mass flow rate(2. 16kg/230ºC)	g/10min	12	ISO  1133- 1
02	Vicat Softening Point (A/50N)	ºC	153	ISO 306
03	Tensile yield stress	Mpa	35	ISO 527- 1,-2
04	Flexural modulus(Ef)	Mpa	1475	ISO 178
05	Charpy notched impact strenth (23ºC)	KJ/m2	3	ISO 306
06	Melt  mass flow rate(2. 16kg/230ºC)	ºC	95	ISO 75B- 1.-2
07	Heat  Distortion Temperature (0.45Mpa)	g/10min	12	ISO  1133- 1

Film Grade
Item	Test condition	Test Method	Value	Unit
Density		ISO 1183	0.944-0.955	g/cm3
MFR	190°C/2.16kg	ISO 1133	0.03-0.07	g/10min
Tensile strength at yield		ISO 527-2	22	MPa
Elongation at break		ISO 527-2	>350	%
ESCR	F50,50°C,100%	ASTM D-1693A	1000	h
VICAT		ASTM D-1525	126	°C
Blown Grade
Item	Test Condition	Test Method	Value	Unit
Density		ISO 1183	0.950~0.955	g/cm
MFR	190°C/2.16kg	ISO 1133	1.7~2.5	g/10min
Tensile strength at yield		ISO 527-2	24	MPa
Elongation at break		ISO 527-2	>600	%
Injection grade
Item	Test Condition	Test Method	Value	Unit
MFR	190°C/2.16kg	ASTM D-1238	20	g/10min
Density	---	ASTM D-792	0.954	g/cm3
Tensile strength at yiled	---	ASTM D-638	28	MPa
Elongation at break	---	ASTM D-638	250	%
Impact tensile strength	---	ASTM D-1822	42	kJ/m2
ESCR		ASTM D-1693	3	---
VACIT	---	ASTM D-1525	127	°C

 

FAQ

 

1. About Quality
All the products must be tested strictly according to the testing procedure before shipment.

2. About Delivery Period
Normally delivered in 7 working days after the confirmation of order& payment.   And it varies according to the material and quantity.

3. About Payment Term
It's flexible, T/T, L/C at sight.

4. About the mode of transportation
(1) by sea
(2) by train

5. If I order in large quantities, can the price be lower?
A: Yes, we can offer a discount for large orders.