HDPE Qhm32f HDPE-RF for Floor Heating Pipe

• CAS No.: 9002-88-4
• Formula: (C2h4)N
• EINECS: 618-339-3
• Model NO.: QHM32F
• Molecular Principal Chain: Carbon Chain Polymer
• Color: White
• Type: Virgin Resin
• Process: Injection Molding/Extrusion Molding/Blow Molding
• Another Namer: Low Pressure Ethylene
• Shape: Pellet - Granules
• MOQ: 1ton
• Quality: High
• Application: Plastic Products
• Transport Package: 25kgs/Bag
• Specification: 25kg
• Origin: China
• HS Code: 3903900000
• Production Capacity: 500000tons

Product Description

 

Description:

QHM32F is a polyethylene resin with hexene-1 as a co-monomer produced by Unipol process of U.C.C., USA. It has the advantages of good flexibility, excellent processing performance, thermal stability and pressure resistance. Mainly used for the production of floor heating pipe, aluminum - plastic composite pipe, solar tube.

PE-RT pipe is a new type of non - crosslinked polyethylene material which can be used in hot water pipe. It is a copolymer of ethylene and octene produced by special molecular design and synthesis process, with a controllable number of branched chain and distribution structure of polyethylene varieties. The unique molecular structure makes the material have excellent stress cracking resistance and long-term hydrostatic strength. PE-RT pipe has good flexibility, and its bending modulus is 550 MPa, and the internal stress generated by bending is low. In this way, it is avoided that the pipe may be damaged at the bending place due to the stress concentration. When constructed (especially in winter), it does not require special tools or heat to bend. Thermal conductivity of 0. 4 W/ (m·k), comparable to PE-X tube, much higher than PP-R 0. 22 W/ (m·k) and PB 0. 17 W/ (m·k), excellent thermal conductivity, suitable for floor heating pipe

Item		unit	test data
Density		g/10m³	0.9342
Melt flow rate	2.16kg	g/10min	0.60
	21.6kg		20.3
melt flow rate radio		---	34
relative variation		---	0.163
number average molecular weight		---	28728
weight-average molecular weight		---	108280
molecular weight distribution		---	3.8
melting temperature		ºC	126
crystallinity		%	54
Critical shear rate(200ºC)		1/sec	500
Oxidation induction time (210ºC,A1)		min	43
tensile yield stress		MPa	16.6
Nominal strain at fracture		%	>713
flexural modulus		MPa	610
Charpy Notched Impact Strength (23ºC)		KJ/	43
intensity of hydrostatic pressure	20ºC,9.9MPa	h	>688
	95ºC,3.6MPa		>1888
	110ºC,1.9MPa		>1888

Reference Model 

For more categories and models, please ask customer service for information.

 

Domestic and international warehousing and transportation one-stop service,

with the supply of the world's leading brands.

FAQ

 

1. About Quality
All the products must be tested strictly according to the testing procedure before shipment.

2. About Delivery Period
Normally delivered in 7 working days after the confirmation of order& payment.   And it varies according to the material and quantity.

3. About Payment Term
It's flexible, T/T, L/C at sight.

4. About the mode of transportation
(1) by sea
(2) by train

5. If I order in large quantities, can the price be lower?
A: Yes, we can offer a discount for large orders.