High Quality Chemical Polypropylene PP 2500hy Raw Material Resin Granules Virgin PP

• Feature: Biodegradable
• Material: Polypropylene/PP
• Usage: Plastic Products
• Model NO.: PP 2500HY
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection Grade. Extrusion Grade, Injection
• Color: White
• Other Name: Polypropylene Particle PP
• ODM/OEM: Accepted
• Keyword: Polypropylene Resin Virgin PP
• Delivery Time: 5-7 Working Days
• Appearance: Transparent Granule
• Transport Package: 25kg/Bag
• Specification: 100% Virgin PP
• Origin: China
• HS Code: 3902100090
• Production Capacity: 8000tons/Months

Product Description

      Polypropylene, referred to as PP, is a polymer made of propylene by addition polymerization. White waxy material, transparent and light in appearance. The chemical formula is (C3H6)n, the density is 0.89 ~ 0.91g/cm3, flammable, the melting point is 164~170 ° C, the softening is about 155 ° C, and the temperature range is -30 ~ 140 ° C. It can resist the corrosion of acid, alkali, salt solution and a variety of organic solvents below 80ºC, and can decompose under high temperature and oxidation.
     PP-2500HY Which is produced by  China Energy Group Ningxia Coal Industry Co., Ltd,based on NTH's Novolen gas-phase polypropylene technology.The product is produced with polymerized propylene and ethylene as the main raw material,Under the action of a catalyst,through the process of polymerization, separation, granulation, packaging, etc. Widely used in Automobile battery shell, Paint barrel, Pipe plate, Baby carriage motorcycle parts.

No.	Testing item		Unit	PP-B,M,110-60P-020(2500HY)
01	Particle appearance	Color granule	pcs/kg	≤20
		Black granule	pcs/kg	0
		Large granule and small granule	g/kg	Actual measurement
02	Melt mass-flow rate		g/10min	2.0±0.6
03	Total ash		mg/kg	Actual measurement
04	Tensile stress at yield		MPa	≥19
05	Flexural modulus		MPa	Actual measurement
06	Charpy notched impact	23ºC	KJ/m²	Actual measurement
		-20ºC	KJ/m²	Actual measurement
07	Yellow index			≤4.0
08	Rockwell hardness			Actual measurement
09	Temperature of deflection under load(Tf 0.45)		ºC	Actual measurement
10	Moulding shrinkage	Parallel	%	Actual measurement
		Vertical	%	Actual measurement

 

Film Grade
Item	Test condition	Test Method	Value	Unit
Density		ISO 1183	0.944-0.955	g/cm3
MFR	190°C/2.16kg	ISO 1133	0.03-0.07	g/10min
Tensile strength at yield		ISO 527-2	22	MPa
Elongation at break		ISO 527-2	>350	%
ESCR	F50,50°C,100%	ASTM D-1693A	1000	h
VICAT		ASTM D-1525	126	°C
Blown Grade
Item	Test Condition	Test Method	Value	Unit
Density		ISO 1183	0.950~0.955	g/cm
MFR	190°C/2.16kg	ISO 1133	1.7~2.5	g/10min
Tensile strength at yield		ISO 527-2	24	MPa
Elongation at break		ISO 527-2	>600	%
Injection grade
Item	Test Condition	Test Method	Value	Unit
MFR	190°C/2.16kg	ASTM D-1238	20	g/10min
Density	---	ASTM D-792	0.954	g/cm3
Tensile strength at yiled	---	ASTM D-638	28	MPa
Elongation at break	---	ASTM D-638	250	%
Impact tensile strength	---	ASTM D-1822	42	kJ/m2
ESCR		ASTM D-1693	3	---
VACIT	---	ASTM D-1525	127	°C

FAQ

 

1. About Quality
All the products must be tested strictly according to the testing procedure before shipment.

2. About Delivery Period
Normally delivered in 7 working days after the confirmation of order& payment.   And it varies according to the material and quantity.

3. About Payment Term
It's flexible, T/T, L/C at sight.

4. About the mode of transportation
(1) by sea
(2) by train

5. If I order in large quantities, can the price be lower?
A: Yes, we can offer a discount for large orders.