PP 1100n Homopolymer Injection Molding Grade Polypropylene Granules Particles Best PP

• Feature: Biodegradable
• Material: Polypropylene/PP
• Usage: Plastic Products
• Model NO.: PP 1100N
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection Grade. Extrusion Grade, Injection
• Color: White
• Other Name: Polypropylene Particle PP
• ODM/OEM: Accepted
• Keyword: Polypropylene Resin Virgin PP
• Delivery Time: 5-7 Working Days
• Appearance: Transparent Granule
• Transport Package: 25kg/Bag
• Specification: 100% Virgin PP
• Origin: China
• HS Code: 3902100090
• Production Capacity: 8000tons/Months

Product Description

      Polypropylene, referred to as PP, is a polymer made of propylene by addition polymerization. White waxy material, transparent and light in appearance. The chemical formula is (C3H6)n, the density is 0.89 ~ 0.91g/cm3, flammable, the melting point is 164~170 ° C, the softening is about 155 ° C, and the temperature range is -30 ~ 140 ° C. It can resist the corrosion of acid, alkali, salt solution and a variety of organic solvents below 80ºC, and can decompose under high temperature and oxidation.

     PP 1100N is a polypropylene homopolymer produced using Novolen gas-phase polymerization technology. The product is made from polymerized propylene as the main raw material, and is manufactured through processes such as polymerization, separation, granulation, and packaging.

PP 1100N
Physical Property	Standard	Value	Unit
Melt Flow Rate	GB/T 3682	12	g/10min
Mechanical behavior	Standard	Value	Unit
Tensile strength yield 50mm/min	GB/T 1040	34.5	Mpa
Tensile strength break 50mm/min	GB/T 1040		Mpa
Elongation yield	GB/T 1040	9.5	%
Flexural modulus	GB/T 9341	1690	Mpa
Izod notch impact	GB/T 1843	3.16	kJ/m2

Film Grade
Item	Test condition	Test Method	Value	Unit
Density		ISO 1183	0.944-0.955	g/cm3
MFR	190°C/2.16kg	ISO 1133	0.03-0.07	g/10min
Tensile strength at yield		ISO 527-2	22	MPa
Elongation at break		ISO 527-2	>350	%
ESCR	F50,50°C,100%	ASTM D-1693A	1000	h
VICAT		ASTM D-1525	126	°C
Blown Grade
Item	Test Condition	Test Method	Value	Unit
Density		ISO 1183	0.950~0.955	g/cm
MFR	190°C/2.16kg	ISO 1133	1.7~2.5	g/10min
Tensile strength at yield		ISO 527-2	24	MPa
Elongation at break		ISO 527-2	>600	%
Injection grade
Item	Test Condition	Test Method	Value	Unit
MFR	190°C/2.16kg	ASTM D-1238	20	g/10min
Density	---	ASTM D-792	0.954	g/cm3
Tensile strength at yiled	---	ASTM D-638	28	MPa
Elongation at break	---	ASTM D-638	250	%
Impact tensile strength	---	ASTM D-1822	42	kJ/m2
ESCR		ASTM D-1693	3	---
VACIT	---	ASTM D-1525	127	°C

 

FAQ

 

1. About Quality
All the products must be tested strictly according to the testing procedure before shipment.

2. About Delivery Period
Normally delivered in 7 working days after the confirmation of order& payment.   And it varies according to the material and quantity.

3. About Payment Term
It's flexible, T/T, L/C at sight.

4. About the mode of transportation
(1) by sea
(2) by train

5. If I order in large quantities, can the price be lower?
A: Yes, we can offer a discount for large orders.